Te fè nan fib amyant, kawoutchou ak chalè-reziste materyèl procesna, konpresyon li nan epè papye.
|
:
4600 x 1500 x (0.3 - 6.0) mm, 4100 x 1500 x (0.3 - 6.0) mm
3800 x 2700 x (0.3 - 6.0) mm, 2000 x 1500 x (0.5 - 6.0) mm
1500 x 1360 x (0.5 - 6.0) mm, 3810 x 1270 x (0.5 - 6.0) mm
1270 x 1270 x (0.5 - 6.0) mm, 1500 x 1500 x (0.5 - 6.0) mm
Lòt gwosè a se opsyonèl oswa selon kondisyon ki nan kliyan yo.
Anbalaj:nan palèt an bwa nan sou 1000 kgs, 2000kgs nèt chak.
|
Linèt kawotchou Asbesto Fizik
GB / T 3985-2008 |
||||||||
|
Item
|
KXB510
|
KXB450
|
KXB400
|
KXB350
|
KXB300
|
KXB250
|
KXB200
|
KXB150
|
|
Tensil fòs MPa
|
21.0
|
18.0
|
15.0
|
12.0
|
9.0
|
8.0
|
6.0
|
5.0
|
|
Granmoun koyefisyan
|
0.9
|
|||||||
|
Boule Pèt
|
28.0
|
30.0
|
||||||
|
Konpresyon pousantaj%
|
7-17
|
|||||||
|
Rebondisman%
|
45
|
40
|
35
|
|||||
|
Krip detant to%
|
50
|
|||||||
|
Dansite g / cm3
|
1.6 - 2.0
|
|||||||
|
Pousantaj koule azòt
[ml / (h.mm)]
|
500
|
|||||||
|
Chalè ak rezistans presyon
|
ak tanperati 500-510
ak presyon nan 13-14MPa, Kenbe pou 30 min san ponksyon
|
ak tanperati a nan 440-450
ak presyon nan 11-12MPa, Kenbe pou 30 min san ponksyon
|
ak tanperati a nan 390-400
ak presyon nan8-9 MPa, Kenbe pou 30 min san ponksyon |
ak tanperati a nan 340-350
ak presyon nan7-8 Mpa, Kenbe pou 30 min san ponksyon |
ak tanperati a nan 290-300
ak presyon nan4-5 MPa, Kenbe pou 30 min san ponksyon |
ak tanperati a nan 240-250
ak presyon nan3-4Mpa, Kenbe pou 30 min san ponksyon |
ak tanperati a nan 190-200
ak presyon nan2-3MPa, Kenbe pou 30 min san |
ak tanperati a nan 140-150
ak presyon nan 1.5-2MPa,Keep for 30 min without puncture
|